- Product Type: Alumina – Silica product, Regular Castable
- Maximum Recommended Temperature: 1650°C
- Main Component: Low iron chamotte
- Type of Bond: Hydraulic
- Appearance: Dry, for addition of water
- Packaging: Sacks
- Shelf Life: 12 months
- Installation Method: Vibrating
- Maximum Grain Size: 6 mm
- Material Required: 2.23 T/m³
- Drinking Water Required for Mixing on Site: 10.0 / 10.4 litres per 100 kg of dry material
- Guidelines: Installation Nr 5
Calde Cast F 60 CO – CASTABLE GERMANY
Data Sheet
Product Data Sheet
| Name | Value |
|---|---|
| Al₂O₃ (EN ISO 1927-3) | 59.0% |
| SiO₂ (EN ISO 1927-3) | 34.0% |
| Fe₂O₃ (EN ISO 1927-3) | 4.5% |
| CaO (EN ISO 1927-3) | 0.7% |
| Property Name |
|---|
| Bulk density after drying at 110°C: 2.29 g/cm³ (EN ISO 1927-6) after firing at 800°C: 2.21 g/cm³ (EN ISO 1927-6) |
| Cold crushing strength after drying at 110°C: 50 MPa (EN ISO 1927-6) after firing at 800°C: 50 MPa (EN ISO 1927-6) after firing at 1200°C: 30 MPa (EN ISO 1927-6) after firing at 1600°C: 95 MPa (EN ISO 1927-6) |
| Permanent linear change after firing at 800°C: -0.1% (EN ISO 1927-6) after firing at 1200°C: -0.1% (EN ISO 1927-6) after firing at 1600°C: -1.2% (EN ISO 1927-6) |
| Thermal conductivity at a mean temperature of 800°C: 1.18 W/mK (EN ISO 1927-8) at a mean temperature of 1000°C: 1.17 W/mK (EN ISO 1927-8) at a mean temperature of 1200°C: 1.31 W/mK (EN ISO 1927-8) |
| Carbon monoxide resistance EN ISO 12676: AVB |
| Reversible thermal expansion after firing [20–1000°C] 0.67% |